Wironium plus
WIRONIUM® plus, premium Cobalt-chrome partial denture alloy
Partial dentures par excellence
Enhanced version of the top-quality alloy WIRONIUM®.
Can be used universally in the field of combination work and clasp partial dentures.
Problem-free processing using the BEGO partial denture system.
Very low thermal conductivity means high wearing comfort for the patient.
Increased elongation limit and high modulus of elasticity for high resistance to possible deformations caused by masticatory forces.
The high elongation limit minimises the danger of clasp fractures.
Controlled carbon content ensures excellent laser welding properties.
Biocompatible and corrosion-resistant.
Type 5: Indicated for prosthetic restorations where parts thereof require a combination of high rigidity and strength, e.g. thin removable partial dentures, sections with thin cross-sections, clasps.
Product details
Composition in % by mass | |
|---|---|
Co 62.5 · Cr 29.5 · Mo 5.0 · Mn 1.5 · Si 1.0 · C · N · Ta | |
Alloy characteristics | Standard values |
Type (ISO 22674) | 5 |
Density | 8,2 g/cm3 |
Preheating temperature | 950–1 050 °C |
Solidus, liquidus temperature | 1345, 1390 °C |
Casting temperature approx. | 1 440 °C |
Young’s modulus | 240 GPa |
Proof strength (Rp0,2) | 715 MPa |
Ultimate strength (Rm) | 1010 MPa |
Elongation after fracture (A5) | 14 % |
Vickers hardness | 350 HV10 |
Availability | REF |
WIRONIUM® plus, 1 kg | 50190 |
Accessoires | REF |
Wiroweld, Co-Cr laser wire, carbon-free, Ø 0,35 mm | 50003 |
Wiroweld, Co-Cr laser wire, carbon-free, Ø 0,5 mm | 50005 |
Cobalt-chrome solder | 52520 |
WIRONIUM® plus tip : With particularly slender partial denture constructions, inaccessible areas should be polished with a handpiece brush to prevent deformations and avoid material reduction at unplanned points on the cast object.
Partial dentures par excellence
Enhanced version of the top-quality alloy WIRONIUM®.
Can be used universally in the field of combination work and clasp partial dentures.
Problem-free processing using the BEGO partial denture system.
Very low thermal conductivity means high wearing comfort for the patient.
Increased elongation limit and high modulus of elasticity for high resistance to possible deformations caused by masticatory forces.
The high elongation limit minimises the danger of clasp fractures.
Controlled carbon content ensures excellent laser welding properties.
Biocompatible and corrosion-resistant.
Type 5: Indicated for prosthetic restorations where parts thereof require a combination of high rigidity and strength, e.g. thin removable partial dentures, sections with thin cross-sections, clasps.