Wirobond C

Wirobond® C – Cobalt-chrome metal-to-ceramic alloy

  • Nickel- and beryllium-free.

  • Simple processing thanks to reliable casting time recognition.

  • Carbon-free composition – particularly well suited for laser welding.

  • The element cerium ensures high bond strength with the ceramic, minimising the risk of subsequent flaking or chipping.

  • Low thermal conductivity – protects the pulp and ensures high wearing comfort for the patient.

  • Biocompatible and corrosion-resistant thanks to a firmly-adhering passive layer.

  • Type 4: Indicated for prosthetic restorations or sections thereof with thin cross-sections exposed to very high loads, e.g. removable partial dentures, clasps, veneered crowns, long-span bridgework or bridges with small cross-sections, bars, retainers, implant-supported superstructures.


Product details

Composition in % by mass


Co 63.3 · Cr 24.8 · W 5.3 · Mo 5.1 · Si 1.0 · Ce


Alloy characteristics

Standard values

Type (ISO 22674)

4

Density

8,5 g/cm3

Preheating temperature

900-1 000 °C

Solidus, liquidus temperature

 1 360, 1 420 °C

Casting temperature approx.

1 500 °C

Young’s modulus

 180 GPa

Proof strength (Rp0,2)

440 MPa

Ultimate strength (Rm)

 780 MPa

Elongation after fracture (A 5)

 16 %

Vickers hardness

 310 HV10

Coefficient of thermal expansion (CTE)

25–500 °C, 10-6 K-1

14,3

Availability

REF

Wirobond® C, 1 kg

50115

Wirobond® C, 250 gr

50116

Accessories

REF

Wiroweld CoCr laser wire, carbon-free, Ø 0,35 mm

50003

Wiroweld CoCr laser wire, carbon-free, Ø 0,5 mm

50005

Wirobond® soldering rods

52622


  • Nickel- and beryllium-free.

  • Simple processing thanks to reliable casting time recognition.

  • Carbon-free composition – particularly well suited for laser welding.

  • The element cerium ensures high bond strength with the ceramic, minimising the risk of subsequent flaking or chipping.

  • Low thermal conductivity – protects the pulp and ensures high wearing comfort for the patient.

  • Biocompatible and corrosion-resistant thanks to a firmly-adhering passive layer.

  • Type 4: Indicated for prosthetic restorations or sections thereof with thin cross-sections exposed to very high loads, e.g. removable partial dentures, clasps, veneered crowns, long-span bridgework or bridges with small cross-sections, bars, retainers, implant-supported superstructures.