Wirobond 280

Wirobond® 280 – The non-precious premium alloy for more than 10 years

Wirobond® 280 is setting standards in the non-precious metal-to-ceramic alloy segment because of a Vickers hardness of 280 HV10, it can be finished to a particularly high standard.

  • Extremely corrosion resistant thanks to the optimal interaction of the indispensable elements chrome and molybdenum.

  • Very good melting and casting properties.

  • No prolonged cooling necessary*, even with large spans.

  • Secure bonding with ceramics.

  • High strength irrespective of the span size, and therefore a wide range of indications.

  • Reliable processing in accordance with the proven BEGO system.

  • Biocompatible and corrosion-resistant

  • Type 5: Indicated for prosthetic restorations where parts thereof require a combination of high rigidity and strength, e.g. thin removable partial dentures, sections with thin cross-sections, clasps.

* Exceptions: Creation (Willi Geller), Reflex® (Wieland Dental + Technik GmbH & Co. KG)

Product details

Composition in % by mass


Co 60.2 · Cr 25.0 · W 6.2 · Mo 4.8 · Ga 2.9 · Mn · Si


Alloy characteristics

Standard values

Type (ISO 22674)

5

Density

8,5 g/cm3

Preheating temperature

900-1 000 °C

Solidus, liquidus temperature

1 355, 1 430 °C

Casting temperature approx.

1 500 °C

Young’s modulus

215 GPa

Proof strength (Rp0,2)

515 MPa

Ultimate strength (Rm)

680 MPa

Elongation after fracture (A 5)

14 %

Vickers hardness

280 HV10

Coefficient of thermal expansion (CTE)

25–500 °C, 10-6 K-1

14,3

Availability

REF

Wirobond® 280, 1 kg

50134

Wirobond® 280, 250 gr

50135

Accessories

REF

Wiroweld CoCr laser wire, carbon-free, Ø 0,35 mm

50003

Wiroweld CoCr laser wire, carbon-free, Ø 0,5 mm

50005

Wirobond® soldering rods

52622


Wirobond® 280 is setting standards in the non-precious metal-to-ceramic alloy segment because of a Vickers hardness of 280 HV10, it can be finished to a particularly high standard.

  • Extremely corrosion resistant thanks to the optimal interaction of the indispensable elements chrome and molybdenum.

  • Very good melting and casting properties.

  • No prolonged cooling necessary*, even with large spans.

  • Secure bonding with ceramics.

  • High strength irrespective of the span size, and therefore a wide range of indications.

  • Reliable processing in accordance with the proven BEGO system.

  • Biocompatible and corrosion-resistant

  • Type 5: Indicated for prosthetic restorations where parts thereof require a combination of high rigidity and strength, e.g. thin removable partial dentures, sections with thin cross-sections, clasps.

* Exceptions: Creation (Willi Geller), Reflex® (Wieland Dental + Technik GmbH & Co. KG)

Related products

Add a Title

Information request for the product: 

Wirobond 280

Province or territory
bottom of page