Wirobond C+ (SLM powder)
Wirobond® C+ – Cobalt-chrome restorations produced with the SLM method
Optimal material characteristics of a cobalt-chrome alloy
Controlled manufacturing process – for stress-free frames and outstanding accuracy of fit
The SLM (Selective Laser Melting) procedure guarantees a homogeneous and extremely dense structure for secure ceramic veneering
Nickel- and beryllium-free – no cytotoxic or allergic potential
Indications :
Frames for partially and fully veneered solutions with up to 16 units and up to four pontics
Fully anatomical crowns and bridges with up to 16 units and up to four pontics
Two-piece abutments
C&B tertiary frame
Retention per segment
Product details
Chemical composition in % | |
|---|---|
Co 63,9 · Cr 24,7 · W 5,4 · Mo 5,0 · Si 1.0 | |
Alloy characteristics | Standard values |
Type (ISO 22674) | 5 |
Density | 8,6 g/cm3 |
0.2% elongation limit (Rp0,2) | 1090 MPa |
Tensile strength (Rm) | 1315 MPa |
Modulus of elasticity | 215 GPa |
Solidus temperature; liquidus temperature | 1 380, 1 420 °C |
Solidus temperature; liquidus temperature | 14,3 |
Dureté (HV10) | 395 |
Availability | REF |
Wirobond® C+, 5 kg | 50512 |
Optimal material characteristics of a cobalt-chrome alloy
Controlled manufacturing process – for stress-free frames and outstanding accuracy of fit
The SLM (Selective Laser Melting) procedure guarantees a homogeneous and extremely dense structure for secure ceramic veneering
Nickel- and beryllium-free – no cytotoxic or allergic potential
Indications :
Frames for partially and fully veneered solutions with up to 16 units and up to four pontics
Fully anatomical crowns and bridges with up to 16 units and up to four pontics
Two-piece abutments
C&B tertiary frame
Retention per segment