PlatinLloyd 100 - Au 72.0%
High-gold, extra-hard alloy for crowns and bridges, gold-yellow, palladium-free.
Gold-yellow – improved aesthetics
Palladium-free – also suitable for sensitive patients
Medium grain size 25 µm – high corrosion resistance
Commercially available since 1992 and accepted worldwide – no known incompatibilities
Wide range of indications – cost-saving
Product details
Composition in % by mass | |
|---|---|
Au 72.0 · Ag 13.7 · Cu 9.8 · Pt 3.5 · Ir · Zn | |
Alloy characteristics | Standard values |
Type (ISO 22674) | 4 |
BEGO GOLD Colour Code | 3 |
Density | 15.5 g/cm3 |
Preheating temperature | 700 °C |
Solidus, liquidus temperature | 900, 940 °C |
Casting temperature | 1 050 °C |
Young’s modulus | 95 GPa |
Proof strength (Rp0,2) | 500 MPa |
Ultimate strength (Rm) | 700 MPa |
Elongation after fracture (A 5) | 15 % |
Vickers hardness | 220 HV5 |
Availability | REF |
PlatinLloyd® 100, 25gr* | 61020 |
Accessories | REF |
Laser welding wire: PlatinLloyd® 100 wire Ø 0,35 mm | 61152 |
BEGO-GOLD-Lot I solder | 61017 |
BEGO-GOLD-Lot II solder | 61043 |
Minoxyd Flux | 52530 |
*Price per gram, fluctuating daily. Sold in 25gr pack.
The BEGO GOLD Colour Code
The areas of colours within the characteristic fields approximately correspond to the intensity of the alloy colours.
Images and illustrations are examples; colours, symbols, designs and information on the depicted labels and/or packaging may differ from reality.
Gold-yellow – improved aesthetics
Palladium-free – also suitable for sensitive patients
Medium grain size 25 µm – high corrosion resistance
Commercially available since 1992 and accepted worldwide – no known incompatibilities
Wide range of indications – cost-saving
Related products