AuroLloyd M - Au 54.0%
Reduced Gold content Alloy, for Crowns and Bridges.
Product details
Composition in % by mass | |
Au 54.0 · Ag 29.0 · Cu 8.0 · Pd 5.0 · In 1.9 · Pt 1.0 · Zn 1 · Ir | |
Alloy characteristics | Standard values |
Type (ISO 22674) | 4 |
BEGO GOLD Colour Code | 5 |
Density | 13.5 g/cm3 |
Preheating temperature | 700 °C |
Solidus, liquidus temperature | 860, 920 °C |
Casting temperature | 1 100 °C |
Young’s modulus | 107 GPa |
Proof strength (Rp0,2) | 455 MPa |
Ultimate strength (Rm) | 860/870 MPa |
Elongation after fracture (A 5) | 6 % |
Vickers hardness | 250 HV5 |
Availability | REF |
AuroLloyd® M, 25gr* | 61054 |
Accessories | REF |
BEGO-GOLD-Lot I solder | 61017 |
BEGO-GOLD-Lot II solder | 61043 |
Minoxyd Flux | 52530 |
*Price per gram, fluctuating daily. Sold in 25gr pack.
The BEGO GOLD Colour Code
The areas of colours within the characteristic fields approximately correspond to the intensity of the alloy colours.
Images and illustrations are examples; colours, symbols, designs and information on the depicted labels and/or packaging may differ from reality.